Attenuation-adjusted deep learning of pore defects in 2D radiographs of additive manufacturing powders
0
Sign in to get full access
Overview
- The paper explores using deep learning models to detect pore defects in 2D radiographs of additive manufacturing powders.
- The researchers developed a novel attenuation-adjusted deep learning approach to account for the effects of powder attenuation on the radiograph images.
- The model was trained and evaluated on a dataset of radiographs of powder samples with known pore defects.
Plain English Explanation
The paper discusses a new way to use deep learning, a type of AI, to find small holes or gaps (called "pore defects") in 3D printed metal parts. These defects can be hard to spot, but they're important to detect because they can weaken the parts and cause problems.
The researchers developed a deep learning model that's designed to work with 2D X-ray images (called "radiographs") of the metal powders used in 3D printing. The key innovation is that the model adjusts for how the powder material affects the X-ray images, making it better able to identify the pore defects.
They trained and tested the model using a dataset of X-ray images of powder samples where the pore defects were already known. The results show the model is effective at detecting these hard-to-find flaws in the 3D printing process. This could help manufacturers improve the quality and reliability of their 3D printed metal parts.
Technical Explanation
The paper presents an attenuation-adjusted deep learning approach to detect pore defects in 2D radiographs of additive manufacturing powders. The model is designed to account for the effects of powder attenuation, which can obscure the visibility of pore defects in the X-ray images.
The researchers developed a convolutional neural network architecture that takes the radiograph images as input and outputs the location and size of detected pore defects. To address the attenuation issue, they incorporated an attenuation adjustment module into the network.
The model was trained and evaluated on a dataset of radiographs of powder samples with known pore defects. The results show the attenuation-adjusted model outperformed a baseline deep learning approach that did not account for powder attenuation.
Critical Analysis
The paper provides a novel and promising approach for detecting pore defects in additive manufacturing using deep learning. The attenuation adjustment module is a key innovation that helps the model overcome a significant challenge in this domain.
However, the paper does not discuss the computational efficiency or inference speed of the model, which would be an important practical consideration for deployment in industrial settings. Additionally, the model was evaluated on a relatively small dataset, so further testing on larger and more diverse datasets would be needed to assess its generalization capabilities.
The paper also does not address potential issues around the reliability and interpretability of the model's predictions. As these deep learning systems are deployed in safety-critical manufacturing applications, it will be important to ensure they are robust and can provide explanations for their outputs.
Conclusion
This paper presents an attenuation-adjusted deep learning approach for detecting pore defects in additive manufacturing powders using 2D radiographs. The key innovation is the incorporation of an attenuation adjustment module to account for the effects of the powder material on the X-ray images.
The results demonstrate the effectiveness of this approach compared to a baseline deep learning model. This work has promising implications for improving the quality control and reliability of 3D printed metal parts, which is crucial for the broader adoption of additive manufacturing in industries like aerospace and automotive.
However, further research is needed to address practical deployment challenges and ensure the robustness and interpretability of the model's predictions. Overall, this paper represents an important step forward in the application of deep learning to additive manufacturing defect detection.
This summary was produced with help from an AI and may contain inaccuracies - check out the links to read the original source documents!
Related Papers
0
Attenuation-adjusted deep learning of pore defects in 2D radiographs of additive manufacturing powders
Andreas Bjerregaard, David Schumacher, Jon Sporring
The presence of gas pores in metal feedstock powder for additive manufacturing greatly affects the final AM product. Since current porosity analysis often involves lengthy X-ray computed tomography (XCT) scans with a full rotation around the sample, motivation exists to explore methods that allow for high throughput -- possibly enabling in-line porosity analysis during manufacturing. Through labelling pore pixels on single 2D radiographs of powders, this work seeks to simulate such future efficient setups. High segmentation accuracy is achieved by combining a model of X-ray attenuation through particles with a variant of the widely applied UNet architecture; notably, F1-score increases by $11.4%$ compared to the baseline UNet. The proposed pore segmentation is enabled by: 1) pretraining on synthetic data, 2) making tight particle cutouts, and 3) subtracting an ideal particle without pores generated from a distance map inspired by Lambert-Beers law. This paper explores four image processing methods, where the fastest (yet still unoptimized) segments a particle in mean $0.014s$ time with F1-score $0.78$, and the most accurate in $0.291s$ with F1-score $0.87$. Due to their scalable nature, these strategies can be involved in making high throughput porosity analysis of metal feedstock powder for additive manufacturing.
Read more8/6/2024
🤿
0
ThermoPore: Predicting Part Porosity Based on Thermal Images Using Deep Learning
Peter Myung-Won Pak, Francis Ogoke, Andrew Polonsky, Anthony Garland, Dan S. Bolintineanu, Dan R. Moser, Michael J. Heiden, Amir Barati Farimani
We present a deep learning approach for quantifying and localizing ex-situ porosity within Laser Powder Bed Fusion fabricated samples utilizing in-situ thermal image monitoring data. Our goal is to build the real time porosity map of parts based on thermal images acquired during the build. The quantification task builds upon the established Convolutional Neural Network model architecture to predict pore count and the localization task leverages the spatial and temporal attention mechanisms of the novel Video Vision Transformer model to indicate areas of expected porosity. Our model for porosity quantification achieved a $R^2$ score of 0.57 and our model for porosity localization produced an average IoU score of 0.32 and a maximum of 1.0. This work is setting the foundations of part porosity Digital Twins based on additive manufacturing monitoring data and can be applied downstream to reduce time-intensive post-inspection and testing activities during part qualification and certification. In addition, we seek to accelerate the acquisition of crucial insights normally only available through ex-situ part evaluation by means of machine learning analysis of in-situ process monitoring data.
Read more4/29/2024
🔮
0
In-situ surface porosity prediction in DED (directed energy deposition) printed SS316L parts using multimodal sensor fusion
Adithyaa Karthikeyan, Himanshu Balhara, Abhishek Hanchate, Andreas K Lianos, Satish TS Bukkapatnam
This study aims to relate the time-frequency patterns of acoustic emission (AE) and other multi-modal sensor data collected in a hybrid directed energy deposition (DED) process to the pore formations at high spatial (0.5 mm) and time (< 1ms) resolutions. Adapting an explainable AI method in LIME (Local Interpretable Model-Agnostic Explanations), certain high-frequency waveform signatures of AE are to be attributed to two major pathways for pore formation in a DED process, namely, spatter events and insufficient fusion between adjacent printing tracks from low heat input. This approach opens an exciting possibility to predict, in real-time, the presence of a pore in every voxel (0.5 mm in size) as they are printed, a major leap forward compared to prior efforts. Synchronized multimodal sensor data including force, AE, vibration and temperature were gathered while an SS316L material sample was printed and subsequently machined. A deep convolution neural network classifier was used to identify the presence of pores on a voxel surface based on time-frequency patterns (spectrograms) of the sensor data collected during the process chain. The results suggest signals collected during DED were more sensitive compared to those from machining for detecting porosity in voxels (classification test accuracy of 87%). The underlying explanations drawn from LIME analysis suggests that energy captured in high frequency AE waveforms are 33% lower for porous voxels indicating a relatively lower laser-material interaction in the melt pool, and hence insufficient fusion and poor overlap between adjacent printing tracks. The porous voxels for which spatter events were prevalent during printing had about 27% higher energy contents in the high frequency AE band compared to other porous voxels. These signatures from AE signal can further the understanding of pore formation from spatter and insufficient fusion.
Read more6/26/2024
🤷
0
An unsupervised approach towards promptable defect segmentation in laser-based additive manufacturing by Segment Anything
Israt Zarin Era, Imtiaz Ahmed, Zhichao Liu, Srinjoy Das
Foundation models are currently driving a paradigm shift in computer vision tasks for various fields including biology, astronomy, and robotics among others, leveraging user-generated prompts to enhance their performance. In the Laser Additive Manufacturing (LAM) domain, accurate image-based defect segmentation is imperative to ensure product quality and facilitate real-time process control. However, such tasks are often characterized by multiple challenges including the absence of labels and the requirement for low latency inference among others. Porosity is a very common defect in LAM due to lack of fusion, entrapped gas, and keyholes, directly affecting mechanical properties like tensile strength, stiffness, and hardness, thereby compromising the quality of the final product. To address these issues, we construct a framework for image segmentation using a state-of-the-art Vision Transformer (ViT) based Foundation model (Segment Anything Model) with a novel multi-point prompt generation scheme using unsupervised clustering. Utilizing our framework we perform porosity segmentation in a case study of laser-based powder bed fusion (L-PBF) and obtain high accuracy without using any labeled data to guide the prompt tuning process. By capitalizing on lightweight foundation model inference combined with unsupervised prompt generation, we envision constructing a real-time anomaly detection pipeline that could revolutionize current laser additive manufacturing processes, thereby facilitating the shift towards Industry 4.0 and promoting defect-free production along with operational efficiency.
Read more6/27/2024